<?xml version="1.0" encoding="utf-8"?>
|
|
<CutterMaterial>
|
|
<Name>High-Speed Steel (HSS) - M35</Name>
|
|
<Note>Cobalt-enriched high-speed steel with improved heat resistance and red hardness compared to M2</Note>
|
|
<ElasticModulus_GPa>215</ElasticModulus_GPa>
|
|
<TensileStrength_MPa>3300</TensileStrength_MPa>
|
|
<ThermalExpansionCoefficient_dMK>10.8</ThermalExpansionCoefficient_dMK>
|
|
<HeatConductivity_WdmK>25.0</HeatConductivity_WdmK>
|
|
<HeatCapacity_JdgK>0.45</HeatCapacity_JdgK>
|
|
<Density_gdcm3>8.10</Density_gdcm3>
|
|
<PoissonRatio>0.30</PoissonRatio>
|
|
<MeltingTemperature_K>1723</MeltingTemperature_K>
|
|
<FusionLatentHeat_Jdg>275</FusionLatentHeat_Jdg>
|
|
<FrictionCoefficient>0.39</FrictionCoefficient>
|
|
<TemperatureVsHardnessCurve>
|
|
<Entry Temperature_K="298">9000</Entry>
|
|
<Entry Temperature_K="873">7500</Entry>
|
|
<Entry Temperature_K="1013">5500</Entry>
|
|
<Entry Temperature_K="1173">3500</Entry>
|
|
<Entry Temperature_K="1273">3500</Entry>
|
|
<Entry Temperature_K="1373">3500</Entry>
|
|
<Entry Temperature_K="1473">3500</Entry>
|
|
</TemperatureVsHardnessCurve>
|
|
<TemperatureVsWearCoefficientCurve>
|
|
<Entry Temperature_K="298">1.70</Entry>
|
|
<Entry Temperature_K="473">2.30</Entry>
|
|
<Entry Temperature_K="673">4.50</Entry>
|
|
<Entry Temperature_K="873">12.00</Entry>
|
|
<Entry Temperature_K="973">22.00</Entry>
|
|
<Entry Temperature_K="1073">35.00</Entry>
|
|
<Entry Temperature_K="1173">55.00</Entry>
|
|
<Entry Temperature_K="1273">85.00</Entry>
|
|
<Entry Temperature_K="1373">125.00</Entry>
|
|
<Entry Temperature_K="1473">180.00</Entry>
|
|
</TemperatureVsWearCoefficientCurve>
|
|
</CutterMaterial>
|