<CutterMaterial>
|
|
<Name>Al2O3-TiC</Name>
|
|
<Note>Alumina ceramic with titanium carbide, offering excellent wear resistance and thermal stability for high-speed machining of cast iron and hardened steels</Note>
|
|
<ElasticModulus_GPa>400</ElasticModulus_GPa>
|
|
<TensileStrength_MPa>700</TensileStrength_MPa>
|
|
<ThermalExpansionCoefficient_dMK>8.5</ThermalExpansionCoefficient_dMK>
|
|
<HeatConductivity_WdmK>35</HeatConductivity_WdmK>
|
|
<HeatCapacity_JdgK>0.80</HeatCapacity_JdgK>
|
|
<Density_gdcm3>4.30</Density_gdcm3>
|
|
<PoissonRatio>0.24</PoissonRatio>
|
|
<MeltingTemperature_K>2323</MeltingTemperature_K>
|
|
<FusionLatentHeat_Jdg>1100</FusionLatentHeat_Jdg>
|
|
<FrictionCoefficient>0.32</FrictionCoefficient>
|
|
<TemperatureVsHardnessCurve>
|
|
<Entry Temperature_K="298">22500</Entry>
|
|
<Entry Temperature_K="873">21200</Entry>
|
|
<Entry Temperature_K="1013">20100</Entry>
|
|
<Entry Temperature_K="1173">18700</Entry>
|
|
<Entry Temperature_K="1273">17500</Entry>
|
|
<Entry Temperature_K="1373">16200</Entry>
|
|
<Entry Temperature_K="1473">14800</Entry>
|
|
</TemperatureVsHardnessCurve>
|
|
<TemperatureVsWearCoefficientCurve>
|
|
<Entry Temperature_K="298">0.65</Entry>
|
|
<Entry Temperature_K="473">0.82</Entry>
|
|
<Entry Temperature_K="673">1.25</Entry>
|
|
<Entry Temperature_K="873">2.10</Entry>
|
|
<Entry Temperature_K="973">3.45</Entry>
|
|
<Entry Temperature_K="1073">5.80</Entry>
|
|
<Entry Temperature_K="1173">9.40</Entry>
|
|
<Entry Temperature_K="1273">15.20</Entry>
|
|
<Entry Temperature_K="1373">24.50</Entry>
|
|
<Entry Temperature_K="1473">38.00</Entry>
|
|
</TemperatureVsWearCoefficientCurve>
|
|